still looking for p-1 ??? [IMG] I have to wonder if this is the same stuff in a reasonable amount???...
not feeling like making a new thread here is P1 Catalyst on Ebay, it looks like this guy purchased some stuff from a closing foundry or robbed...
So What Im hearing is we need to tell all the Guys trying to cast aluminum cans that they need to mix that mess half and half with a BMW rim:p...
definitely signs of some Zinc in there, and who knows what else!... Aluminum doesn't like Pb, so if you picked up some of that from a Babbit...
What im hoping for, always great input from the members here V/r HT1
OK I love What Bruce did for me, but I want to "pro " it up so I priced up tools and parts: first off I could find nothing off the Shelf In SAE...
one side
Bruce, AKA Crazybillybob hooked me up with these amazing 3D printed Flask hardware i told him to sell the files online . I'm curious how long...
I use Shellac to seal matchplates before I do anything , over fillets I use Auto Body Primer then Steel wool , normally I have to add a second...
those are not your 0nly options what are you making
Clean yes, but not degas... Specifics Smelting, Not melting is a refining process to remove unwanted (stuff) specific elements (say Lead from...
did the K bond start to smoke when the flames went out??? V/r HT1 P.S. Inquiring minds want to know.
I wish he had kept that video private , he has the same Drill press as me, which sort of blows my trepidation out of the water .... save as a...
Plaster will not "Just dry" it has to be baked , a plaster expert will chime in Gassy metal? Maybe, you already got good advice on clean metal...
I really like that "Cleat Design" it still has the issue of needing a pretty good Drill press and an Angle plate to finish them, but I cannot...
ive never seen a pro flask tha t was not a bit of a sand catcher, Mifco's current being the absolute worse...
your going to have to go through a foundry supply to get petrobond clay https://piedmontfoundrysupply.com/products-test-page/ or maybe these...
it does not matter save when it does , and it alternates back and forth , most often you want pins facing up, so when you place the drag on the...
I would not expect hate from you, But production foundries cannot tolerate the potential failures this technique will cause, and FNG's trying it...
if your supplier is going back to p-1 they will need to carry the catalyst the original literature DOES NOT indicate additional catalyst being...