Yes, you are right i did look more in detaile and the lost was will be differemt. Thanks for input!
I can do lost foam casting process simulation. However, I have not done it even close as much as simulations in greensand. In short I can create...
Hello! New week new simulations. Wanted to share with you this case study of ductile iron (EN 500-14 grade) cover. I most of grey iron castings...
[MEDIA] I did made simulation by tilting the whole by 3 deg. Sorry will take too much time to make all the 3 simulations. As you can see it...
Yes. This is what we always look for - worst case scenario. It can be that pourer do not keep the pouring basing full and for such situation the...
Hi. Wanted to give some good example on what we do in foundry when failure happens time to time and there is need for more detailed investigation...
Welcome Jonny. Impressive results casting aluminium. I usually simulate cast iron casting technology and calculate gating systems, but would love...
Very interesting to see your work. I must later write some thread about gating calculatins and feeder size.
This sand core for venting the riser must be something used very long time ago. the most simple way is to make notch / V shape or cone shape like...
Only visually looks like hot/warm crackin:...
Generally speaking the riser would solidify first. The place where you see the defect is last place to solidify. Because of the geometry looks...
Does the riser is located only at one end of the casting? Does the defect appeared bottom of riser or other location?